http://tapatalk.imageshack.com/v2/15...665047badd.jpg
Printable View
farout!
Working on one for myself tonight, similar to the last one I posted. Will post finished pics tomorrow.
http://i1286.photobucket.com/albums/...ps8wlt7mpx.jpg
http://tapatalk.imageshack.com/v2/15...9ecaf8bae8.jpg
Working on some new prodo
Sent from my iPhone using Tapatalk
Here's the pics of the finished piece. It's not as clean as the last one I did, but it'll do for me. Kinda messed up my encalmo section cause I wasn't paying as much attention as I should have been. Didn't really start to focus until I already messed it up. Also used old scrap tube for most of it, and you can see it in the fume. Can tell the tube was still a little dirty due to the "spottiness" of the fume, but I think that looks cool. Adds some more variation to the fume. Not my cleanest bends either. Functions beautifully though. I'm really just being really picky about most of this stuff too, but that's just how I am. Nothing's ever good enough. lol
http://i1286.photobucket.com/albums/...psp6i0smif.jpg
http://i1286.photobucket.com/albums/...psmmr994tt.jpg
http://i1286.photobucket.com/albums/...pswsavsrht.jpg
http://i1286.photobucket.com/albums/...psjzyiklwu.jpg
http://i1286.photobucket.com/albums/...ps1ybotkbq.jpg
http://i1286.photobucket.com/albums/...psveydu7z4.jpg
http://i1286.photobucket.com/albums/...pskavqab78.jpg
http://i1286.photobucket.com/albums/...psvnaybyor.jpg
http://i1286.photobucket.com/albums/...psoyxwqcbo.jpg
Implosions are fun
http://i.imgur.com/PVBrQwB.jpg
http://i.imgur.com/OGfzUEp.jpg
Made this hollow space pendant out of some scrap last night, but the opal exploded in the kiln overnight. Thought it was pretty cool though up until that. The space tube was a piece of scrap left over from the sherlock up above, and the opal was a big old opal that had a pretty bad crack in it already. I don't like to break polished opals, so I tried to use it with the crack, and was gonna give it to a friend who really liked the opal when he saw it. Also didn't have as much clear around the opal as I should have. The opal was pretty big to start, weighed in at like .4g if I remember correctly, and I didn't want to have a big marble on it either, so I just went ahead and took the risk. Was properly annealed as well. I guess both things combined were just too much stress for it to handle. Oh well, you win some, you lose some. No big deal since it was all scrap stuff, but still a bummer to see it not survive.
http://i1286.photobucket.com/albums/...psk6sgamoc.jpg
http://i1286.photobucket.com/albums/...psii73dpst.jpg
i think i heard somewhere that you need approximately 2-3 times as much glass around the opal as the opal is wide. What a bummer though that looked sweet, Do you mind telling what the space color is?
Quote:
Originally Posted by mikecgara
Absolutely not true. I skin opals down to less than a mm of clear encasent and stick them right to the surface of things.
Attachment 71803
This galaxy vagina has an opal clitoris with less than 1/2mm skin on top.
i meant with the rough opals, i think the rounded and polished ones don't need nearly as much glass. But if you do that with rough ones too then that's awesome. After the couple of times ive had a crack from too little clear im weary to try again without a good amount.Quote:
Originally Posted by Aymie
Profound recommends having at least as many millimeters of glass on all sides of the opal, as the opal is thick, I believe, and I think that goes especially for rough opals. I too have done a bunch of opals without that much clear on them and gotten away with it more times than not, but that is recommended because when the glass around the opal (or anything for that matter) is thin, it has a much harder time containing the stress during the annealing process. Polished opals seem to not have much trouble no matter how much glass is around it, as long as the opal is not too large, and small rough are usually ok as well, but this one was around 7mil thick most of the way through, already had a crack in it, right before encasment I dropped it and broke a piece off, which made an unpolished rough side, and had less than a 2 mil of clear on most sides. I believe all of these factors combined simply caused way too much stress for it to handle during annealing.
Edit: Mike, the space color is silver filings and gold fume on cobalt, then tube encased in clear.
I bought a gram of opals and only got 2 out of 5 to survive and they got scuzz all around them and didn't look that great. My first time using them though
Sent from my iPhone using Tapatalk
since opals are touchy flame anneal them some, then they bench cool almost every time pretty stress free. ever since i was bugging Bates one time and he said flame anneal everything, its been sinking in more.
obviously Happy Vagina Day is in order here!Quote:
Originally Posted by Aymie
The face of a big ass spoon I'm working on right now. I'm loving the way this one is coming out so far.
http://i1286.photobucket.com/albums/...pshgue2ooz.jpg
i have something too, silver and gold fume, on the bowl and at the joint over heavy blue stardust
Attachment 72091
Attachment 72092
Attachment 72093
Attachment 72094
Attachment 72095
Attachment 72096
Attachment 72097
Dude. cheesenip, my man.
Thanks Paul! Nice slide Steak! Here's some pics of that finished spoon.
http://i1286.photobucket.com/albums/...psso5bn05s.jpg
http://i1286.photobucket.com/albums/...psoame8wrj.jpg
http://i1286.photobucket.com/albums/...psjjinqz8r.jpg
http://i1286.photobucket.com/albums/...pslxzkem0k.jpg
http://i1286.photobucket.com/albums/...psamla96al.jpg
http://i1286.photobucket.com/albums/...pstkno9fgi.jpg
http://i1286.photobucket.com/albums/...psqbkfqtrw.jpg