Some new stuff

hell ya crip. lookin good as always. Im glad to here your lil va jay jay slice is healin . i liked to use 32, or 38 tube for my iso. with the 38 i would just open and lay down lines, no blowin out a bubble then openin, peace

im with ss i use 30 and just lay my lines in there. it seems a lil tight in the beginning but u get used to it and then can do mostly anything sometines i blow it open and then open it but thats when im not in the mood to do a double flare. keep it up man u r progresing sicki.

thx yalll, hey Mex What are you talkin bout double flair fill me in , well i made 2 more yesterday buit one got jacked up and didnt make it..

really clean, great job.

Made 3 more today super thick 3 inch points super condensed Its now easy to flair tube jsut took some practice now its all like butttttter, weeeeeeeeeeeeeeeeeeeee:chilling:

good job crip lookin good gettin easier thats swell keep up the good wook

right on bro! those are startin to look mint. soon you should try fusing multiple sections together for larger peices

crip, the IO skills are getting sweet man. onions right i wouldnt mind seeing a bubbler or something

i like the lighter fumed ones with the pink...whats the light blue colour in the last pic?

Dude lookin really good!
Nick

Those are sweet. You should try to fume a little lighter.

Thx guys ya im tryin to do lighter fume, I guess I gotta do it realllly light cuz it seems light when i put it on jsut a hint of brown but when i reduce it it must bunch it all up , so ya ill try super light nextime,, I guess Im jstu used to burnin most of it off on teh outside stufff

when you fume it shouldn't look like you did anything until to put the tube back in the flame, it just magically appears with a little flicker of the flame.

gotcha i try it tomarrrow all this time i thought i had to see a lil coat hahaha I was puttin it on some till the glass looked like a mirror hehehweeeeee:chilling:

yeah what i do is put a light little coat on, hit it with a slight oxy flame till it goes away, then switch it up to a reducing flame and it will bring out a nice even coat.

well still fumin to hard, i was tryin out some unobtaniums yesterday and i thought it was gona come out sweeeet but I could hear it crackin in the kiln I jsut knew it was that, whats the trick to workin these colors in with out having them crack??, shoud i thin them out with clear first and try that and advise would be great THX the momka greeen dragon was awsome came out sick and no crackin

colours with lots of sparkle like to be worked under an oxi flame, they dont like high garage temps or long kiln times. basicly the was i see it is, youre trying to get it nice and hot once, get the shape done, and pop her in the kiln as soon as possible, and try to do it near the end up your work day so they dont sit and precipitate chrome all day.

hey crip ur stuff is looking good keep it up. a double flare is when u open the end and just draw the lines for your stem then close melt down and stretch stem, then blow a hole at the end of stem and attatch blowtube and then open up other end and draw lines there, then close and blow ur bowl. its how i initially learned but it takes a lil while longer. i would say try it its good to know multiple ways of doing things. im with everyone else, now start mking some dry hammers and side cars. u tried basic sherlocks yet? ur kickin ass man keep goin.

onion is right on about the aventurine colors. if you run the kiln for a long time keep it at 975 for a garage and then bring it up to 1050 to anneal at the end of your work session.

THx guys ya it was the second pice probally garaged for 2 hrs at 1040 then it ramoped up to 1150 for 15 min then cool, so I guess thats not a good idea on sparkle colors, could that be whats makin my fumes come out white tooo theh high kiln temps ??

I think ill try a bubbler today well see what happens

yeah i would fully avoid the striking cycle @1150 with sparkles, its kind of a death wish. like mer said, when your working em turn your kiln down to just under 1000, then pop it up to 1040 as if it were your strike cycle, then ramp down.