Well , I figured you did now that your not in a full time relationship.
as far as your other quote....
So , you implode sheets? You implode rod? You make cane but its not as good? Your comment was vague, so I don't understand.Nomad - I prefer an implosion. I gather on the end of a tube. Then pick it up on the marver. Then encase it with the backing.
Dichro cane is not as good as the sheet dichro.
In all seriousness , can we get a picture of imploded dichro? I can honestly say I have not ever seen any.